Magnet Wire

Enamelled Copper Nickel Resistance Alloy Wire

Enamelled Copper Nickel Resistance Alloy Wires have been broadly used for standard resistors, automobile parts, winding resistors, etc. using the insulation processing best suited for these applications, taking full advantage of the distinctive features of enamel coating.

Resistance Alloy Wire

Enamelled Copper Nickel Resistance Alloy Wires specifications

Insulation: Enamelled Temper Class: :133℃,150℃180℃,200℃,220℃
Colour Of Enamelled: Black,Red,Nature,Blue,Green,yellow Bare Conductor: CuNi,NiCr,FeCrAL,Karma,FeCrAl
Wire Gauge: ≥0.012mm Application: Heating,Precision Resistor
Shape: Round Wire,Flat Wire
High Light: enamel magnet wire, enameled wire

Enamelled Copper Nickel Resistance Alloy Wires features

main property type Cuni1 CuNI2 CuNI6 CuNi8 CuNI10 CuNi14 CuNi19 CuNi23 CuNi30 CuNi34 CuNI44
main chemical composition Ni 1 2 6 8 10 14.2 19 23 30 34 44
MN / / / / / 0.3 0.5 0.5 1.0 1.0 1.0
CU rest rest rest rest rest rest rest rest rest rest rest
max working temperature / 200 220 250 250 300 300 300 350 350 400
density g/cm3 8.9 8.9 8.9 8.9 8.9 8.9 8.9 8.9 8.9 8.9 8.9
resistivity  at 20 °c 0.03 ± 10% 0.05± 10% 0.10± 10% 0.12± 10% 0.15± 10% 0.20± 5% 0.25± 5% 0.30± 5% 0.35± 5% 0.40± 5% 0.49± 5%
temperature coefficient of resistance <100 <120 <60 <57 <50 <38 <25 <16 <10 -0 <-6
tensile strength mpa >210 >220 >250 >270 >290 >310 >340 >350 >400 >400 >420
elongation >25 >25 >25 >25 >25 >25 >25 >25 >25 >25 >25
melting point °c 1085 1090 1095 1097 1100 1115 1135 1150 1170 1180 1280
coefficient of conductivity 145 130 92 75 59 48 38 33 27 25 23

Type of Insulation

Insulation-enamelled Name Thermal Level℃ (working time 2000h) Code Name GB Code ANSI. TYPE
Polyurethane enamelled wire 130 UEW QA MW75C
Polyester enamelled wire 155 PEW QZ MW5C
Polyester-imide enamelled wire 180 EIW QZY MW30C
Polyester-imide and polyamide-imide double coated enameled wire 200 EIWH (DFWF) QZY/XY MW35C
Polyamide-imide enamelled wire 220 AIW QXY MW81C